Benefits of black oxide finish

2.jpg

Black oxide finished bearing components feature a set of special technical characteristics, especially in the case of components that move relative to each other. Multiple protective effects can be achieved if only one functional element (typically the rolling elements) is treated. For best effect, however, all functional surfaces of a rolling element bearing, including the inner and outer ring as well as the rolling elements, should be black oxide finished. The main benefits of using this protection method are summed up below.

Benefit 1: Black oxide finish offers improved run-in and wear characteristics

The conversion layer of the black oxide finish exhibits a marked resistance against wear and bending. This results in favourable run-in characteristics and run-in periods of rolling element bearings and a subsequent trouble-free and long-lasting operation. Wear during run-in is reduced considerably and the run-in period is significantly shorter than that of standard rolling element bearings. In addition, the porous nature of the conversion layer aids in the adhesion and retention of lubricant on the functional surfaces, thereby improving the lubrication conditions especially in the critical run-in and start-up phases.

NKE supplies black oxide finished cylindrical roller bearings (full complement or with cage) to various OEMs for large sized and wind turbine main gear boxes. Besides verifiably lessening the occurrence of WEC (white etching cracks), black oxide finish has been proven to provide additional protection especially during the run-in and testing phase of these gearboxes.

Benefit 2: Improved adhesive wear characteristics with black oxide finish

Rolling bearings operating in low-load situations and bearings that are subjected to rapid speed changes during operation can be susceptible to adhesive wear (slippage damage and smearing). Under these conditions, slippage occurs at the contact area between the rolling elements and most commonly the inner ring raceway, especially when the difference between the rolling speeds between raceway and rolling elements is very high. The resulting slippage, which mainly takes place where the rolling elements enter the load zone, causes smearing. This, in turn, causes lasting damage to the rolling element and raceway’s surfaces and material structure. The operating characteristics of the bearing consequently deteriorate quickly and a premature failure of the bearing is not unusual. This type of damage often occurs where lubrication is insufficient or an unsuitable lubricant is used.

A special type of slippage damage occurs on full complement cylindrical roller bearings where the counteracting surface speeds of the contacting rolling elements prevent the formation of a stable lubricant film to separate the contact surfaces. Here, direct contact between adjacent rolling elements cannot always be avoided so that, as friction increases, smearing and damage to the rolling elements’ lateral surfaces occur.

In both cases, the black oxide finish can act as a protective layer, which delays the onset of wear and smearing. If steel on steel contact occurs due to a short breakdown of the separating lubrication film, the risk of cold shut and other types of severe surface damage is reduced considerably.

Cylindrical roller bearings with a bore diameter smaller than 560m are designed to operate at an operating load of approximately 1% of their dynamic load carrying capacity and with a rotation speed of up to 1,200rpm. Despite design measures to reduce the number of rolling elements and thus the load carrying capacity, the formation of the characteristic arrow or diamond shaped smearing marks in the raceway and corresponding damage to the rolling elements cannot be entirely avoided. NKE resolved this issue effectively by using rolling elements with a black oxide finish and introducing a lubricant chosen specifically for this application.

Benefit 3: Black oxide finish provides protection against environmental effects

In combination with its other advantages, black oxide finish also provides protection against environmental effects. Besides providing better corrosion protection in conjunction with a suitable lubricant, the black oxide layer also helps prevent fretting corrosion and forms a barrier on the bearing steel against harmful hydrogen diffusion and chemical reactions with aggressive lubricant ingredients, such as the wear and corrosion protection additives often found in oils to improve their effectiveness in gear tooth systems.

NKE uses black oxide finishing to further improve the technical properties of rolling bearings. The method has proven itself in practice especially with full complement cylindrical roller bearings, but other types of rolling bearing are also black oxide finished, depending on the application. The company offers a large number of black oxide finished rolling bearings. At NKE, this finish is used especially for cylindrical roller bearings, which then carry the suffix SQ94. The most common variants are SQ94B (rolling elements black oxide finished) and SQ94-D (all bearing components except for the cage black oxide finished).